Case analysis of defective harness forming

-
One. Scorch
Phenomenon characteristics: high-temperature control, temperature control instrument failure (such as poor contact of thermoelectric Europe). b. The gum is very smoky, with a strong smell and a crunchy sound. C. Middle coke-like coke. d. Cracks and pores in the glued joint
Case analysis of defective harness forming
Cause: The temperature control is too high. b. The scorch on the screw has not been cleaned for a long time. C. After a long shutdown, the plastic in the screw will age and decompose. d. If the heating time is too long, the plastic in the screw will age and decompose. e. Change the mold multiple times and change the color to break down the plastic. F. The gland of the machine head is loose, and the rubber material in the clamping channel is kept for a long time, causing aging and decomposition. G. Instrument malfunction.
Solution: Check the heating system. b. Clean the machine head and tighten the screws regularly. C. According to the process of heating, pay attention to the time. d. Change the mold, change the color in time, and clean to prevent noise and scorching. e. Prevent the gland from entering the glue. F. If scorching occurs, immediately clean the machine head and tighten the screws.
Two. Poor plasticization
Phenomenon characteristics: a. There is a toad-like phenomenon. b. Low-temperature control. c. The surface is darkened, there are tiny cracks or unplasticized particles, and the middle is raw rubber. c. There are obvious marks on the glue seam.
Reason: Temperature control is too low or improper control. b. There are resin particles that are difficult to plasticize. c. The screw speed is too fast, the rubber particles have not completely reached the plasticization. d. The quality of raw materials. e. The head pressure is not enough.
Remedy: a. Check the plastic quality. b. Control the temperature according to the process. c. Properly reduce the screw speed and extend the plasticizing time. d. Use cooling to enhance the plasticization and compactness of plastics. e. Reasonably select the mold to increase the pressure of the flue outlet. f. The honeycomb board relies on the screw side to add omentum to strengthen plasticization.
Three. Pimples
Phenomenon: a. There are small crystal points and small particles on the plastic surface. b. There is scorch on the plastic surface (special type glued seam surface). c. The plastic contains impurities. d. Poor plasticization.
Reasons: a. The temperature control is too low, and the unplasticized rubber compound is extruded. b. The quality of the plastic is poor (there are resins that are more difficult to plasticize). c. Impurities are mixed in when feeding. d. High-temperature control, producing scorched pimples. e. It is not tight to the molded cover, causing aging and deterioration after entering the glue. f. The screw is not cleaned, there is old glue. g. The uneven size of plastic particles causes poor plasticization.
Remedy: a. The plastic itself causes pimples, and raise the temperature appropriately. b. Check if there are impurities in the plastic. If impurities are found, clean the machine head and screw to eliminate scorch. c. When the plasticization is poor or resin pimples, increase the temperature properly, and reduce the screw speed. d. Add omentum in front of the honeycomb board.
Four: bubbles, stomata, puffy eyes
Phenomenon characteristics and reasons: a. The temperature is too high, the plastic decomposes to produce gas. b. The plastic is wet or wet. c. Moisture or volatile substances on the wire core or cable core. d. Spilling water droplets on the surface of the polyethylene (PE) plastic that did not enter the sink will form small bubbles.
Remedy: a. The temperature is adjusted properly to prevent the local temperature from being too high. b. Check the quality of the plastic, do not use it when it is wet. c. Dry the plastic to remove moisture and moisture. d. Preheat the wire core or cable core to remove moisture and moisture.

Yeahui is a connector supplier with 11 years of experience in developing high-quality connectors and wiring harnesses. We have many types of products, including obd connector, circular connector, agricultural connector, and so on. We can meet the requirements of various customers. Feel free to learn more about connectors or buy our connectors, looking forward to your message.

评论

发表评论

此博客中的热门博文

What is the Difference Between J1939 Connector Type 1 and 2?

-
图片
  SAE J1939 (hereinafter referred to as J1939) is the recommended standard of the American Society of Automotive Engineers (SAE). It is controlled and communicated by the "Truck and Bus Electrical & Electronics Committee" (Track & Bus Electrical & Electronics Committee). Developed and written by the Track & Bus Control and Communications Network Subcommittee. J1939 has become a recognized industry standard and choice for commercial vehicle diagnostics and data communication heavy, off-highway, truck, bus, ship propulsion, power generation, industrial pumping, construction, and material handling machinery. J1939 is a high-level protocol network (CAN) based on Controller Area. It is widely used by the diesel engine industry to provide diagnostic data such as vehicle engine speed, temperature, oil temperature, exhaust emissions, and other customizable options. J1939 connectors are divided into black and green rubber cores, but do you know the difference between t
阅读全文

Benefits of overmolded connectors and wiring harnesses?

-
图片
What is overmolding? In short, overmolding is an injection molding process in which two or more materials are used to combine a harness wire and a connector to form a single part, and the cable assembly is placed in a mold. In this process, the first material substrate will be covered by other materials. The overmolding process requires the use of insert molding (single injection) or multiple injection molding techniques to cover rigid plastic parts with TPU layers or other overmolding materials. So what are the benefits of the connector and harness overmolding process? Benefits of overmolding connectors and harnesses: 1. Increase the flexibility of the cable harness exit so that most of the movement between the cable harness and the connector occurs at the cable harness exit. 2. Provide abrasion resistance, impact resistance or impact resistance. 3. Fix the cable assembly by sealing the assembly in plastic. 4. Provide 360 degree strain relief and increase tension. 5. Cr
阅读全文

Harness Processing Manufacturing Upgrade

-
图片
In the context of global environmental conservation, new energy vehicles have become an inevitable trend in the development of automobiles worldwide. PwC's first blueprint for the Chinese auto industry, released on December 8, states that China's new energy vehicle sales are far ahead of other markets in the world. With the government's vigorous support for new energy vehicles, China's new energy vehicle era has arrived. Global sales of new energy vehicles reached 500,000 in 2015, of which 330,000 were sold in China, three times the previous year, and far ahead of other markets in the world. Accelerating development, Internet giants and other emerging players are actively entering the market, bringing pressure and shock to traditional car manufacturers and dealers. There is no doubt that new energy and intelligent connected cars have become the mainstream of the automotive industry, and the demand for applicable wiring harnesses will also increase significantly. Au
阅读全文